AvaSpire® AV-621 CF30
Polyaryletherketone
Solvay Specialty Polymers
Technical Data
Product Description
AvaSpire® AV-621 CF30 is a 30% carbon fiber reinforced version of AvaSpire® AV-621. It offers better dimensional stability and warp resistance than 30% carbon fiber reinforced PEEK. The AV-621 CF30 grade offers the highest strength, stiffness, and fatigue resistance of any AV-621 based grade. Furthermore, this resin generally retains most of the desirable ultra-performance attributes of carbon fiber reinforced PEEK including chemical resistance, fatigue resistance, and long term thermal oxidative stability.
The excellent balance of properties of AV-621 CF30 makes this grade well suited for a broad range of applications across a number of industries, including healthcare, transportation, electronics, and chemical processing.
This resin can be easily melt processed by injection molding using standard equipment. The melt processing behavior of AV-621 CF30 is very similar to that of 30% CF reinforced PEEK. The lower melt flow of AV-621 CF30 is well suited for extrusion applications while offering a similar property profile to AV-651 CF30.
General
Material Status • Commercial: Active
Literature 1 • Technical Datasheet
Search for UL Yellow Card • Solvay Specialty Polymers
• AvaSpire®
Availability • Africa & Middle East • Europe • North America
• Asia Pacific • Latin America
Filler / Reinforcement • Carbon Fiber, 30% Filler by Weight
• Fatigue Resistant • Good Dimensional Stability
Features • Flame Retardant • High Heat Resistance • High Strength
• Good Chemical Resistance • High Stiffness
Uses • Medical/Healthcare • Pump Parts • Seals
Applications
RoHS Compliance • Contact Manufacturer
Appearance • Black
Forms • Pellets
Processing Method • Injection Molding • Machining • Profile Extrusion
Physical Nominal Value (English) Nominal Value (SI) Test Method
Specific Gravity 1.42 1.42 g/cm³ ASTM D792
Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) 1.0 g/10 min 1.0 g/10 min ASTM D1238
Molding Shrinkage 3 ASTM D955
Flow : 0.125 in (3.18 mm) 0.0 to 2.0E-3 in/in 0.0 to 0.20 %
Across Flow : 0.125 in (3.18 mm) 9.0E-3 to 0.011 in/in 0.90 to 1.1 %
Water Absorption (24 hr) 0.10 % 0.10 % ASTM D570
Mechanical Nominal Value (English) Nominal Value (SI) Test Method
Tensile Modulus
-- 4 2.49E+6 psi 17200 MPa ASTM D638
-- 3.38E+6 psi 23300 MPa ISO 527-2/1A/1
Tensile Stress
Yield 28400 psi 196 MPa ISO 527-2/1A/5
-- 4 26300 psi 181 MPa ASTM D638
Tensile Elongation
Break 4 2.2 % 2.2 % ASTM D638
Break 2.2 % 2.2 % ISO 527-2/1A/5
Flexural Modulus
-- 2.19E+6 psi 15100 MPa ASTM D790
-- 3.09E+6 psi 21300 MPa ISO 178
AvaSpire® AV-621 CF30
Polyaryletherketone
Solvay Specialty Polymers
Mechanical Nominal Value (English) Nominal Value (SI) Test Method
Flexural Strength
-- 40100 psi 276 MPa ASTM D790
-- 42900 psi 296 MPa ISO 178
Compressive Strength 22000 psi 152 MPa ASTM D695
Shear Strength 13200 psi 91.0 MPa ASTM D732
Impact Nominal Value (English) Nominal Value (SI) Test Method
Notched Izod Impact
-- 1.3 ft•lb/in 69 J/m ASTM D256
-- 4.6 ft•lb/in² 9.6 kJ/m² ISO 180
Unnotched Izod Impact
-- 12 ft•lb/in 640 J/m ASTM D4812
-- 19 ft•lb/in² 39 kJ/m² ISO 180
Hardness Nominal Value (English) Nominal Value (SI) Test Method
Rockwell Hardness (M-Scale) 101 101 ASTM D785
Thermal Nominal Value (English) Nominal Value (SI) Test Method
Deflection Temperature Under Load 5 ASTM D648
264 psi (1.8 MPa), Annealed, 0.126 in (3.20 410 °F 210 °C
mm)
Glass Transition Temperature 320 °F 160 °C ASTM D3418
Peak Melting Temperature 644 °F 340 °C ASTM D3418
CLTE - Flow (-58 to 122°F (-50 to 50°C)) 2.8E-6 in/in/°F 5.0E-6 cm/cm/°C ASTM E831
Specific Heat DSC
122°F (50°C) 0.323 Btu/lb/°F 1350 J/kg/°C
392°F (200°C) 0.433 Btu/lb/°F 1810 J/kg/°C
Thermal Conductivity 2.4 Btu•in/hr/ft²/°F 0.35 W/m/K ASTM E1530
Fill Analysis Nominal Value (English) Nominal Value (SI) Test Method
Melt Viscosity (752°F (400°C), 1000 sec^-1) 790 Pa•s 790 Pa•s ASTM D3835
Injection Nominal Value (English) Nominal Value (SI)
Drying Temperature 300 °F 149 °C
Drying Time 4.0 hr 4.0 hr
Rear Temperature 690 °F 366 °C
Middle Temperature 700 °F 371 °C
Front Temperature 710 °F 377 °C
Nozzle Temperature 720 °F 382 °C
Processing (Melt) Temp 690 to 730 °F 366 to 388 °C
Mold Temperature 300 to 350 °F 149 to 177 °C
Injection Rate Fast Fast
Screw Compression Ratio 2.0:1.0 to 3.0:1.0 2.0:1.0 to 3.0:1.0
Injection Notes
Back Pressure: Minimum