LUVOCOM® 1115-8559
Polyetherketoneketone
Lehmann & Voss & Co.
Technical Data
Product Description
LUVOCOM® 1115-8559 is a Polyetherketoneketone (PEKK) material filled with carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America.
Important attributes of LUVOCOM® 1115-8559 are:
• Chemical Resistant
• Flame Retardant
• Good Stiffness
• Hydrolytically Stable
• Lubricated
Typical application of LUVOCOM® 1115-8559: Engineering/Industrial Parts
General
Material Status • Commercial: Active
Literature 1 • Technical Datasheet
Search for UL Yellow Card • Lehmann & Voss & Co.
• LUVOCOM®
Availability • Africa & Middle East • Europe • North America
• Asia Pacific • Latin America
Filler / Reinforcement • Carbon Fiber
Additive • Lubricant
• Flame Retardant • Good Strength • Low Friction
Features • Good Chemical Resistance • Good Wear Resistance • Lubricated
• Good Stiffness • Hydrolytically Stable • Self Lubricating
Uses • Bearings • Gears
• Bushings • Pump Parts
Appearance • Grey
Physical Nominal Value (English) Nominal Value (SI) Test Method
Density 1.51 g/cm³ 1.51 g/cm³ ISO 1183
Molding Shrinkage 0.30 to 0.60 % 0.30 to 0.60 % DIN 16901
Water Absorption (73°F (23°C), 24 hr) < 0.10 % < 0.10 %
Mechanical Nominal Value (English) Nominal Value (SI) Test Method
Tensile Modulus 2.03E+6 psi 14000 MPa ISO 527-2
Tensile Stress (Break) 23900 psi 165 MPa ISO 527-2
Tensile Strain (Yield) 1.5 % 1.5 % ISO 527-2
Flexural Modulus 1.60E+6 psi 11000 MPa ISO 178
Flexural Stress 32600 psi 225 MPa ISO 178
Flexural Strain at Flexural Strength 2.0 % 2.0 % ISO 178
Impact Nominal Value (English) Nominal Value (SI) Test Method
Charpy Unnotched Impact Strength ISO 179/1eU
73°F (23°C) 14 ft•lb/in² 30 kJ/m²
Thermal Nominal Value (English) Nominal Value (SI) Test Method
Continuous Use Temperature 500 °F 260 °C UL 746B
Maximum Use Temperature - Short Term 572 °F 300 °C
Electrical Nominal Value (English) Nominal Value (SI) Test Method
Surface Resistivity < 1.0E+8 ohms < 1.0E+8 ohms IEC 60093
Insulation Resistance < 1.0E+9 ohms < 1.0E+9 ohms IEC 60167
LUVOCOM® 1115-8559
Polyetherketoneketone
Lehmann & Voss & Co.
Injection Nominal Value (English) Nominal Value (SI)
Drying Temperature
Desiccant Dryer, A 284 °F 140 °C
Desiccant Dryer, B 302 °F 150 °C
Drying Time
Desiccant Dryer, A 4.0 to 6.0 hr 4.0 to 6.0 hr
Desiccant Dryer, B 4.0 to 8.0 hr 4.0 to 8.0 hr
Rear Temperature 698 to 734 °F 370 to 390 °C
Middle Temperature 716 to 788 °F 380 to 420 °C
Front Temperature 734 to 788 °F 390 to 420 °C
Nozzle Temperature 734 to 788 °F 390 to 420 °C
Processing (Melt) Temp 734 °F 390 °C
Mold Temperature 356 to 428 °F 180 to 220 °C
Injection Notes
General
• In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines.
• Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials.
• Lengthy dwell times for the melts in the cylinder should be avoided.
• Lower the temperatures during interruptions!
Predrying (optional)
• It is advisable to predry the granulate with a suitable dryer immediately before processing.
• The granulate may absorb moisture from the air.
Delivery Form & Storage
• Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets.
• Preferably storage should be effected in dry and normally temperatured rooms
Additional Information
• During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment.
• The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application.
• High-temperature polymers place increased demands on the tool steels employed.
• Please contact us for further information.